Nb2O5-doped NiZnCo ferrite ceramics with ultra-high magnetic quality factor and low coercivity for high-frequency electronic devices

This work investigates the influence of niobium pentoxide (Nb₂O₅) as dopant, on the structural, magnetic, and dielectric properties of NiZnCo ferrites. The results showed that Nb₂O₅ was an effective dopant, and the Nb⁵⁺ ions entered the B site to replace Fe³⁺ ions, which altered the electromagnetic properties of the NiZnCo ferrite. In particular, the coercivity (H_c) was 20～24 Oe, and the magnetic quality factor (Q), was more than 200 at x = 0 and x = 0.1 wt%, which is 4～5 times higher than that of NiZn and NiCuZn ferrites. Excellent electromagnetic properties were obtained for 0.1 wt% Nb₂O₅-doped NiZnCo ferrite, i.e., M_s = 88.3 emu/g, H_c =20.4 Oe, ρ = 2.4 × 10⁵ Ω m and Q = 202 @20 MHz. These excellent electromagnetic properties of Nb₂O₅-doped NiZnCo ferrites could be potentially applied to resonators and capacitors at high frequency.     

Good dielectric performance and broadband dielectric polarization in Ag,Nb co-doped TiO2

Due to the demand of miniaturization and integration for ceramic capacitors in electronic components market, TiO₂-based ceramics with colossal permittivity has become a research hotspot in recent years. In this work, we report that Ag⁺/Nb⁵⁺ co-doped (Ag_1/4Nb_3/4)_xTi_1−xO₂ (ANTOx) ceramics with colossal permittivity over a wide frequency and temperature range were successfully prepared by a traditional solid–state method. Notably, compositions of ANTO0.005 and ANTO0.01 respectively exhibit both low dielectric loss (0.040 and 0.050 at 1 kHz), high dielectric permittivity (9.2 × 10³ and 1.6 × 10⁴ at 1 kHz), and good thermal stability, which satisfy the requirements for the temperature range of application of X9R and X8R ceramic capacitors, respectively. The origin of the dielectric behavior was attributed to five dielectric relaxation phenomena, i.e., localized carriers' hopping, electron–pinned defect–dipoles, interfacial polarization, and oxygen vacancies ionization and diffusion, as suggested by dielectric temperature spectra and valence state analysis via XPS; wherein, electron-pinned defect–dipoles and internal barrier layer capacitance are believed to be the main causes for the giant dielectric permittivity in ANTOx ceramics.     

Solution-Synthesized Multifunctional Janus Nanotree Microswimmer

Synthetic active matters are perfect model systems for non-equilibrium thermodynamics and of great potential for novel biomedical and environmental applications. However, most applications are limited by the complicated and low-yield preparation, while a scalable synthesis for highly functional microswimmers is highly desired. In this paper, an all-solution synthesis method is developed where the gold-loaded titania-silica nanotree can be produced as a multi-functional self-propulsion microswimmer. By applying light, heat, and electric field, the Janus nanotree demonstrated multi-mode self-propulsion, including photochemical self-electrophoresis by UV and visible light radiation, thermophoresis by near-infrared light radiation, and induced-charge electrophoresis under AC electric field. Due to the scalable synthesis, the Janus nanotree is further demonstrated as a high-efficiency, low-cost, active adsorbent for water decontamination, where the toxic mercury ions can be reclaimed with enhanced efficiency.     

Optimal Design of Novel Electromagnetic-Ring Active Balancing Actuator with Radial Excitation

Imbalance vibration is a typical failure mode of rotational machines and has significant negative effects on the effii-ciency,accuracy,and service life of equipment.To automatically reduce the imbalance vibration during the opera-tional process,different types of active balancing actuators have been designed and widely applied in actual produc-tion.However,the existing electromagnetic-ring active balancing actuator is designed based on an axial excitation structure which can cause structural instability and has low electromagnetic driving efficiency.In this paper,a novel radial excitation structure and the working principle of an electromagnetic-ring active balancing actuator with a combined driving strategy are presented in detail.Then,based on a finite element model,the performance param-eters of the actuator are analyzed,and reasonable design parameters are obtained.Self-locking torque measurements and comparative static and dynamic experiments are performed to validate the self-locking torque and driving effi-ciency of the actuator.The results indicate that this novel active balancing actuator has sufficient self-locking torque,achieves normal step rotation at 2000 r/min,and reduces the driving voltage by 12.5％.The proposed novel balancing actuator using radial excitation and a combination of permanent magnets and soft-iron blocks has improved electro-magnetic efficiency and a more stable and compact structure.     

Hollow multi-nanochannel carbon nanofiber/MoS2 nanoflower composites as binder-free lithium-ion battery anodes with high capacity and ultralong-cycle life at large current density

The electrode materials with high pseudocapacitance can enhance the rate capability and cycling stabil-ity of lithium-ion storage devices.Herein,we fabricated MoS2 nanoflowers with ultra-large interlayer spacing on N-doped hollow multi-nanochannel carbon nanofibers(F2-MoS2/NHMCFs)as freestanding binder-free anodes for lithium-ion batteries(LIBs).The ultra-large interlayer spacing(0.78～1.11 nm)of MoS2 nanoflowers can not only reduce the internal resistance,but also increase accessible active sur-face area,which ensures the fast Li+intercalation and deintercalation.The NHMCFs with hollow and multi-nanochannel structure can accommodate the large internal strain and volume change during lithi-ation/delithiation process,it is beneficial to improving the cycling stability of LIBs.Benefiting from the above combined structure merits,the F2-MoS2/NHMCFs electrodes deliver a high rate capability 832 mA h g-1 at 10 A g-1 and ultralong cycling stability with 99.29 and 91.60％capacity retention at 10 A g-1 after 1000 and 2000 cycles,respectively.It is one of the largest capacities and best cycling stability at 10 A g-1 ever reported to date,indicating the freestanding F2-MoS2/NHMCFs electrodes have potential applications in high power density LIBs.     

氧化铝纤维束织造过程中摩擦磨损性能研究

运用往复线性摩擦试验方法,搭配自制的摩擦试验夹具,模拟织造过程中氧化铝纤维束-筘齿的摩擦行为,研究加载力、预加张力和摩擦频率对悬空状态下氧化铝纤维束摩擦磨损性能的影响.结果表明:随着加载力的增加,氧化铝纤维束所受摩擦力及长丝断裂根数增加,摩擦系数减小;在预加张力为0.40 N时,氧化铝纤维束所受摩擦力和摩擦系数出现最小值,磨损程度也最小;在摩擦稳定阶段,摩擦频率增加,则氧化铝纤维束所受摩擦力先下降,后略有上升,当摩擦频率增加至5 Hz时,氧化铝纤维束的摩擦系数较1 Hz时增加18.7％,磨损程度也最为严重.     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

New optical ceramics: High-entropy sesquioxide X2O3 multi-wavelength emission phosphor transparent ceramics

Highly transparent X₂O₃ sesquioxide ceramics were obtained from a solid solution of five different oxides (Lu₂O₃, Y₂O₃, Yb₂O₃, Gd₂O₃, and Dy₂O₃), mixed in an equal molar ratio according to the principle of high-entropy. The fabricated (Lu, Y, Yb, Gd, Dy)₂O₃ ceramics achieved 99.97 % of the relative density and exhibited a high degree of optical transparency with the in-line transmittance of almost 80 % in the visible wavelength range. Emissions of Gd³⁺ (⁶P_J → ⁸S_7/2 at 312 nm), Dy³⁺ (⁴F_9/2 → ⁶H_15/2 at 492 nm and ⁴F_9/2 → ⁶H_13/2 at 572 nm), and Yb³⁺ (²F_5/2 → ²F_7/2 at 1031 nm) suggested a potential application of the high-entropy ceramics as multi-wavelength emission phosphor transparent ceramics. High-entropy ceramics also exhibited lower specific heat and thermal conductivity compared to single-element sesquioxide ceramics. This work demonstrated that highly transparent oxide ceramics, with complex chemical compositions and good optical properties, could be obtained using the high-entropy principle.     

Eco-friendly and degradable red phosphorus nanoparticles for rapid microbial sterilization under visible light

Pathogens pose a serious challenge to environmental sanitation and a threat to public health.The frequent use of chemicals for sterilization in recent years has not only caused secondary damage to the environment but also increased pathogen resistance to drugs,which further threatens public health.To address this issue,the use of non-chemical antibacterial means has become a new trend for environmental disinfection.In this study,we developed red phosphorus nanoparticles(RPNPs),a safe and degradable photosensitive material with good photocatalytic and photothermal properties.The red phosphorus nanoparticles were prepared using a template method and ultrasonication.Under the irradiation of simulated sunlight for 20 min,the RPNPs exhibited an efficiency of 99.98%in killing Staphylococcus aureus due to their excellent photocatalytic and photothermal abilities.Transmission electron microscopy and ultraviolet–visible spectroscopy revealed that the RPNPs exhibited degradability within eight weeks.Both the RPNPs and their degradation products were nontoxic to fibroblast cells.Therefore,such RPNPs are expected to be used as a new type of low-cost,efficient,degradable,biocompatible,and eco-friendly photosensitive material for environmental disinfection.